匯總了常用的國標、行標、團標中應力腐蝕實驗方法標準，分享如下：

3、GB/T 15970.3-1995 金屬和合金的腐蝕 應力腐蝕試驗 第3部分:U型彎曲試樣的制備和應用 Corrosion of metals and alloys-Stress corrosion testing-Part 3: Preparation and use of U-bend specimens

4、GB/T 15970.4-2000 金屬和合金的腐蝕 應力腐蝕試驗 第4部分：單軸加載拉伸試樣的制備和應用 Corrosion of metals and alloys-Stress corrosion testing-Part 4:Preparation and use of uniaxially loaded tension specimens

5、GB/T 15970.5-1998 金屬和合金的腐蝕 應力腐蝕試驗 第5部分:C型環試樣的制備和應用 Corrosion of metals and alloy—Stress corrosion testing—Part 5:Preparation and use of C-ring specimens

6、GB/T 15970.6-2007 金屬和合金的腐蝕 應力腐蝕試驗 第6部分：恒載荷或恒位移下的預裂紋試樣的制備和應用 Corrosion of metals and alloys—Stress corrosion testing—Part 6:Preparation and use of pre-cracked specimens for tests under constant load or constant displacement

7、GB/T 15970.7-2017 金屬和合金的腐蝕 應力腐蝕試驗 第7部分: 慢應變速率試驗 Corrosion of metals and alloys—Stress corrosion testing—Part 7:Slow strain rate testing

8、GB/T 15970.8-2005 金屬和合金的腐蝕 應力腐蝕試驗 第8部分 焊接試樣的制備和應用 Corrosion of metals and alloys—Stress corrosion test—Part 8:Preparation and use of speciments to evaluate weldments

9、 GB/T 15970.9-2007 金屬和合金的腐蝕 應力腐蝕試驗 第9部分：漸增式載荷或漸增式位移下的預裂紋試樣的制備和應用 Corrosion of metals and alloys—Stress corrosion testing—Part 9:Preparation and use of pre-cracked speciments for tests under rising load or rising displacement

10、GB/T 15970.10-2021 金屬和合金的腐蝕 應力腐蝕試驗 第10部分：反向U型彎曲試驗方法 Corrosion of metals and alloys—Stress corrosion testing—Part 10:Reverse U-bend method

實驗設備-高溫、高壓、應力腐蝕

11、GB/T 15970.11-2022 金屬和合金的腐蝕 應力腐蝕試驗 第11部分:金屬和合金氫脆和氫致開裂試驗指南 Corrosion of metals and alloys—Stress corrosion cracking—Part 11:Guidelines for testing the resistance of metals and alloys to hydrogen embrittlement and hydrogen-assisted cracking 

12、GB/T 15972.33-2024 光纖試驗方法規范 第33部分：機械性能的測量方法和試驗程序 應力腐蝕敏感性參數 Specifications for optical fibre test methods—Part 33:Measurement methods and test procedures for mechanical characteristics— Stress corrosion susceptibility 

13、GB/T 20122-2006 金屬和合金的腐蝕 滴落蒸發試驗的應力腐蝕開裂評價 Corrosion of metals and alloys—Evaluation of stress corrosion cracking by the drop evaporation test

14、GB/T 22640-2023 鋁合金應力腐蝕敏感性評價試驗方法 Test method for determining susceptibility to stress corrosion cracking of aluminium alloys

15、GB/T 24518-2009 金屬和合金的腐蝕 應力腐蝕室外暴露試驗方法 Corrosion of metals and alloys—Test methods for stress corrosion cracking in outdoor environments

16、 GB/T 25996-2019 絕熱材料對奧氏體不銹鋼外部應力腐蝕開裂的試驗方法 Test method for thermal insulations on external stress corrosion cracking of austenitic stainless steel

17、GB/T 33883-2017 7XXX系鋁合金應力腐蝕試驗 沸騰氯化鈉溶液法 Test methods for stress corrosion of 7××× series aluminum alloys—Boiling sodium chloride solution method

18、GB/T 36676-2018 埋地鋼質管道應力腐蝕開裂(SCC)外檢測方法 External inspection methodology of stress corrosion cracking(SCC)forburied steel pipelines

19、GB/T 40339-2021 金屬和合金的腐蝕 服役中檢出的應力腐蝕裂紋的重要性評估導則 Corrosion of metals and alloys—Guidelines for assessing the significances of stress corrosion cracks detected in service

20、 GB/T 40403-2021 金屬和合金的腐蝕 用四點彎曲法測定金屬抗應力腐蝕開裂的方法 Corrosion of metals and alloys—Methodology for determining the resistance of metals to stress corrosion cracking using the four-point bend method 

硫化氫腐蝕實驗室設施及設備

21、GB/T 4157-2017 金屬在硫化氫環境中抗硫化物應力開裂和應力腐蝕開裂的實驗室試驗方法 Laboratory testing of metals for resistance to sulfide stress crackingand stress corrosion cracking in H2S environment

22、 GB/T 42661-2023 金屬和合金的腐蝕 模擬海洋環境中鋼筋應力腐蝕敏感性試驗方法  Corrosion of metals and alloys—Test method for determining susceptibility to stress corrosion of steel reinforcement in simulated marine environment

23、 GB/T 43925-2024 套管和油管全尺寸拉伸應力腐蝕試驗方法 Test method for full-scale tensile stress corrosion testing of casing and tubing

24、 MH/T 6072-2019 飛機發動機清洗用化學品對鈦合金應力腐蝕的試驗方法 

25、SY/T 0599-2018 天然氣地面設施抗硫化物應力開裂和應力腐蝕開裂金屬材料技術規范

26、SY/T 7348-2016 鋼質管道及儲罐腐蝕評價標準 第 4部分： 埋地鋼質管道應力腐蝕開裂直接評價 NACE RP0204-2004,MOD

27、T/CAPEC 46-2024 金屬在硫化氫環境中抗硫化物應力開裂和應力腐蝕開裂試驗監理技術要求 Supervision technical requirements for testing of metals for resistance to sulfide stress cracking and stress corrosion cracking in H2S environment

28、T/CCTAS 55-2023  軌道交通車輛用抗應力腐蝕鋁合金材料過程控制要求 Preparation process requirements for stress corrosion control of aluminum alloy materials used in rail transit vehicles

29、T/CNS 13-2019 核電廠金屬材料高溫高壓水中模擬輻照促進應力腐蝕開裂敏感性試驗方法 Test method for simulated-irradiation assisted stress corrosion cracking susceptibility in high temperature pressurized water of metallic materials for nuclear power plants

30、 T/CNS 5-2018 核電廠金屬材料高溫高壓水中應力腐蝕裂紋擴展試驗方法 Test method for stress corrosion crack growth in high temperature pressurized water of metallic materials for nuclear power plants 

常見應力腐蝕標準試驗方法對比及應用

31、YB/T 5344-2006 鐵-鉻-鎳合金在高溫水中應力腐蝕試驗方法 Fe-Cr-Ni alloys-stress corrosion test in high temperature water

32、YB/T 5362-2006 不銹鋼在沸騰氯化鎂溶液中應力腐蝕試驗方法 Test method for stress corrosion-cracking resistance of stainless steels in a boiling magnesium chloride solution 

33、YS/T 814-2012 黃銅制成品應力腐蝕試驗方法 Test method for stress corrosion resistance of brass finished products 

34、GB/T 45879-2025 金屬和合金的腐蝕 應力腐蝕敏感性電化學快速試驗方法 Corrosion of metals and alloys-Electrochemical methods for fast test of stress corrosion cracking susceptibility

幾種應力腐蝕試樣實物圖如下，依次是U型彎曲、三點彎曲、四點彎曲、C型環試樣；